III nitride crystal and method for producing same

ABSTRACT

A group III nitride crystal having a small dislocation density and good quality and a production method for the group III nitride crystal are provided. The production method for the group III nitride crystal is characterized by growing a group III nitride crystal film  2  on a substrate  1 , depositing a metallic film  3  thereon and, then, not only changing the metallic film  3  into a metallic nitride film  4  and, further, generating a pore  4   h , but also forming a void portion  2   b  in the group III nitride crystal film  2  by performing a thermal treatment and, thereafter, filling the void portion  2   b  by a group III nitride crystal  5  for filling by further growing a group III nitride crystal and, subsequently, growing a group III nitride crystal  6  on the metallic nitride film  4.

TECHNICAL FIELD

The present invention relates to a group III nitride crystal and a production method for the group III nitride crystal and, particularly, to a group III nitride having a low dislocation density and good quality, and a production method for the group III nitride crystal.

BACKGROUND ART

A group III nitride crystal such as Al_(x)Ga_(y)In_(1-x-y)N crystal (0≦x, 0≦y, x+y≦1) appears in the limelight as a material for a Light Emitting Diode (hereinafter, referred to as “LED”) or a Laser Diode (hereinafter, referred to as “LD”) and is expected to be deployed as an electronic device element.

However, it is difficult to grow the group III nitride crystal in bulk crystal growth and, accordingly, a self-supporting substrate of the group III nitride crystal has not been obtained. A substrate of the group III nitride crystal which is presently in practical use is a sapphire substrate and a method in which the group III nitride crystal is epitaxially grown on a single crystal sapphire substrate by, for example, a Metalorganic Vapor Phase Epitaxy (hereinafter, referred to as “MOVPE”) method has ordinarily been employed.

Meanwhile, since the sapphire substrate is different in a lattice constant from the Al_(x)Ga_(y)In_(1-x-y)N crystal, even when the Al_(x)Ga_(y)In_(1-x-y)N crystal is grown directly on the sapphire substrate, a single crystal can not be obtained.

Thus, a method in which, firstly, a buffer layer of the Al_(x)Ga_(y)In_(1-x-y)N crystal is grown on the sapphire substrate at a low temperature and, then, the Al_(x)Ga_(y)In_(1-x-y)N crystal is then grown on the buffer layer has been proposed (refer to, for example, JP-A No. 63-188983). By providing such buffer layer, a strain between a lattice of the substrate and that of the Al_(x)Ga_(y)In_(1-x-y)N crystal was relaxed, to thereby realize an epitaxial growth of the Al_(x)Ga_(y)In_(1-x-y)N single crystal. However, even in such method, by a strain between the substrate and the lattice of the Al_(x)Ga_(y)In_(1-x-y)N crystal, a dislocation of from 10⁹ to 10¹⁰ cm⁻² is generated, to thereby cause a problem in preparing the LD or the like.

In order to reduce a dislocation density, a method in which a GaN layer is grown on the sapphire substrate and, thereafter, a metallic layer is deposited on the thus-grown GaN layer and, subsequently, the resultant article is thermally treated to form a void portion in the GaN layer which is then filled by performing the GaN crystal growth and, thereafter, the GaN crystal is grown on the metallic layer has been proposed (refer to, for example, JP-A No. 2002-343728).

DISCLOSURE OF THE INVENTION

At present growth of group III nitride crystals other than a GaN crystal has not been conducted by the aforementioned method.

Under these circumstances, an object of the present invention is to provide not only the GaN crystal but also a group III nitride crystal having a small dislocation density and good quality and a production method for these crystals.

In order to attain the aforementioned object, a production method for a group III nitride crystal according to the present invention is characterized by comprising the steps of:

-   -   growing a group III nitride crystal film on a substrate;     -   depositing a metallic film on the group III nitride crystal         film;     -   not only generating a pore in the metallic film, but also         forming a void portion in the group III nitride crystal film by         thermally treating the substrate on which the group III nitride         crystal film is grown and the metallic film is deposited;     -   growing a group III nitride crystal for filling on the group III         nitride crystal film in which the void portion is formed in an         atmosphere of an oxygen concentration of 0.1% by mol or less to         fill the void portion in the group III nitride crystal film; and     -   growing a group III nitride crystal on the metallic film in an         atmosphere of an oxygen concentration of 0.1% by mol or less.

Further, a production method for a group III nitride crystal according to the present invention is characterized by comprising the steps of:

-   -   growing a group III nitride crystal film on a substrate;     -   depositing a metallic film on the group III nitride crystal         film;     -   not only changing the metallic film into a metallic nitride         film, and further, generating a pore in the metallic film, but         also forming a void portion in the group III nitride crystal         film by thermally treating the substrate on which the group III         nitride crystal film is grown and the metallic film is         deposited;     -   growing a group III nitride crystal for filling on the group III         nitride crystal film in which the void portion is formed in an         atmosphere of an oxygen concentration of 0.1% by mol or less to         fill the void portion in the group III nitride crystal film; and     -   growing a group III nitride crystal on the metallic nitride film         in an atmosphere of an oxygen concentration of 0.1% by mol or         less.

Further, a group III nitride crystal according to the present invention is obtained by the aforementioned method for obtaining the group III nitride crystal.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a diagram explaining a production method for a group III nitride crystal according to the present invention.

BEST MODE FOR CARRYING OUT THE INVENTION

One production method for a group III nitride crystal according to the present invention, in reference to FIG. 1, comprises the step of growing a group III nitride crystal film 2 on a substrate 1 as shown in FIG. 1A, the step of depositing a metallic film 3 on the group III nitride crystal film 2 as shown in FIG. 1B, the step of obtaining a group III nitride crystal portion 2 a in which, not only a pore 4 h is generated in the metallic layer, but also a void portion 2 b is formed in the group III nitride crystal film 2 by thermally treating the substrate on which the group III nitride crystal film is grown and the metallic film is deposited as shown in FIG. 1C, the step of filling the void portion in the group III nitride crystal film 2 by growing a group III nitride crystal 5 for filling (the group III nitride crystal grown for the purpose of filling the void portion in the group III nitride crystal film) on the group III nitride crystal portion 2 a in which the void portion 2 b is formed in an atmosphere of an oxygen concentration of 0.1% by mol or less as shown in FIG. 1D, and the step of growing a group III nitride crystal 6 on the metallic film in an atmosphere of an oxygen concentration of 0.1% by mol or less as shown in FIG. 1E.

By growing the group III nitride crystal 5 for filling in the void portion 2 b in the group III nitride crystal film 2 generated by performing a thermal treatment after the group III nitride crystal film 2 and the metallic film 3 are formed to fill the void portion 2 b and, further, growing the group III nitride crystal 6 on the metallic film in which the pore 4 h is generated by the thermal treatment, a strain caused by a difference in a lattice constant between the substrate 1 and the group III nitride crystal 6 can be eliminated. Therefore, the thermal treatment is satisfactory provided that it is performed at a temperature necessary for forming the void portion in the group III nitride film. Under these circumstances, it is preferable that the temperature of the thermal treatment be 700° C. or more.

Further, by defining the atmosphere at the time of growing the group III nitride crystal 5 for filling in the void portion 2 b and growing the group III nitride crystal 6 on the metallic film in which the pore 4 h is generated as an oxygen concentration of 0.1% by mol or less, a wide range of group III nitride crystals including not only a GaN crystal, but also an Al_(x)Ga_(y)In_(1-x-y)N crystal can favorably be grown. When the oxygen concentration is over 0.1% by mol, a dislocation density becomes large and an oxide may be generated or a spot defect to be caused by mixing of an oxygen ion may be generated thus inhibiting a favorable growth of the group III nitride crystal. From the standpoint of allowing the dislocation density to be small, the oxygen concentration is more preferably 0.01% by mol or less.

Another production method for the group III nitride crystal according to the present invention, in reference to FIG. 1, comprises the step of growing the group III nitride crystal film 2 on the substrate 1 as shown in FIG. 1A, the step of depositing the metallic film 3 on the group III nitride crystal film 2 as shown in FIG. 1B, the step of not only changing the metallic film 3 into a metallic nitride film 4 and generating the pore 4 h in the metallic nitride film 4, but also forming the void portion 2 b in the group III nitride crystal film 2 by thermally treating the substrate on which the group III nitride crystal film 2 is grown and the metallic film is deposited as shown in FIG. 1C, the step of filling the void portion in the group III nitride crystal film 2 by growing the group III nitride crystal 5 for filling on the group III nitride crystal film 2 in which the void portion 2 b is formed in an atmosphere of an oxygen concentration of 0.1% by mol or less as shown in FIG. 1D, and the step of growing the group III nitride crystal 6 on the metallic nitride film 4 in an atmosphere of an oxygen concentration of 0.1% by mol or less as shown in FIG. 1E.

By performing a thermal treatment after the group III nitride crystal film 2 and the metallic film 3 are formed, at least a surface of the metallic film 3 is ordinarily nitrided to form the metallic nitride film 4 and, in order to promote nitriding of the metallic film, it is preferable that an N₂ gas or a gas containing a nitrogen atom (for example, NH₃ gas) be added as a nitrogen source at the time of the thermal treatment. In such a manner of generating the metallic nitride, forming of the pore 4 h is promoted to facilitate the growth of the group III nitride crystal 5 for filling in the void portion 2 b.

On the other hand, by performing the thermal treatment, even when the surface of the metallic film 3 is not nitrided, provided that at least the pore 4 h is formed in the metallic film 3 and, further, the void portion 2 b is formed in the group III nitride crystal film 2, at the time of forming the group III nitride crystal in an atmosphere of an oxygen concentration of 0.1% by mol or less, the group III nitride crystal is preferentially grown in the void portion 2 b through the pore generated in the metallic film as the group III nitride crystal 5 for filling, to thereby fill the void portion 2 b; therefore, the strain caused by the difference in the lattice constant between the substrate 1 and the group III nitride crystal 6 can be eliminated. On this occasion, according to the present invention, a reducing atmosphere of an oxygen concentration of 0.1% by mol or less is formed as an atmosphere at the time of growing the group III nitride crystal for filling and the group III nitride crystal. The method of forming the atmosphere of an oxygen concentration of 0.1% by mol or less is not particularly limited provided that it does not go counter to the object of the present invention. For example, a method in which, in addition to the N₂ gas or the NH₃ gas being used as a nitrogen source, and the H₂ gas being used as an oxygen reducing agent, a method using carbon or the like is mentioned as a favorable method. It is also favorable to use these methods simultaneously. On this occasion, when the H₂ gas which is an oxygen reducing gas and the NH₃ gas which is a nitrogen raw material gas are concurrently present, it is considered that oxygen is removed by a reaction represented by the formula (1) to be described below. In such case as described above, a molar ratio of the H₂ gas to the NH₃ gas is preferably 10% or more. When the molar ratio is less than 10%, it is considered that an oxygen reduction effect is reduced. 3H₂+2NH₃+O₂→2NH₄+2H₂O  (1).

As for carbon (C), activated carbon, a carbon plate made of carbon, or the like is favorably used. When carbon is used, it is preferable to use carbon having a surface area (hereinafter, referred to also as “unit surface area”), based on 1 m³ of an entire raw material gas, of 100 cm²/m³ or more.

In the production method for the group III nitride crystal according to the present invention, as for group III nitride crystals, an Al_(x)Ga_(y)In_(1-x-y)N crystal is preferable. In the group III nitride crystal, the Al_(x)Ga_(y)In_(1-x-y)N crystal is extremely useful as a material for an LED or LD.

In the production method for the group III nitride crystal according to the present invention, as for metallic films, titanium, vanadium or an alloy comprising at least one of titanium and vanadium is favorably mentioned. Metals or alloys other than these metals or the alloy can be used provided that they have a catalytic action of promoting decomposition of the group III nitride crystal film. For example, Fe, Ni, Zr, Hf, W, Pt or an alloy comprising at least one metal element of these metals can be mentioned.

Further, the thickness of the metallic film is preferably from 10 nm to 1000 nm. In a case in which the thickness is less than 10 nm, when nitriding is performed, even when it is over 1000 nm the metallic film is liable to be peeled off, and it is difficult to generate the pore. Still further, in view of generating a stable pore, the thickness of the metallic film is more preferably from 20 nm to 500 nm.

Further, in the production method for the group III nitride crystal according to the present invention, only the group III nitride crystal grown on the metallic film on the substrate can be obtained by removing the substrate. A method of removing the substrate is not particularly limited, and a method of removing the substrate by grinding or laser irradiation while the substrate is held, a method of separating the substrate having a different thermal expansion coefficient from the group III nitride crystal film by heat shock or the like can favorably be used.

Further, still another production method for the group III nitride crystal according to the present invention comprises the step of further growing a group III nitride crystal on the group III nitride crystal obtained by the aforementioned production method for the group III nitride crystal in an atmosphere of an oxygen concentration of 0.1% by mol or less. The production method for the group III nitride crystal according to the present invention can be applied to multiple-stage growth of the group III nitride crystal, and allows the thickness of a layer of the group III nitride crystal having a small dislocation density to be large or allows the layers of two types or more of the group III nitride crystals each having a small dislocation density to be formed.

The group III nitride crystal according to the present invention can be obtained by the aforementioned production method. By the production method, not only can the strain caused by the difference in the lattice constant between the substrate and the group III nitride crystal be eliminated, but also the oxygen concentration at the time of growing the group III nitride crystal be maintained at such a low concentration as 0.1% by mol or less and, accordingly the group III nitride crystal having a small dislocation density and good quality can be obtained.

EXAMPLES

Hereinafter, the present invention will more specifically be described with reference to the embodiments.

Example 1

In reference to FIG. 1, as shown in FIG. 1A, a 200 nm AlN crystal film which is a group III nitride crystal film 2 was grown on a sapphire substrate which is a substrate 1 by using an MOCVD method. On this occasion, trimethyl aluminum and NH₃ were used as a group III raw material and a nitrogen raw material, respectively. Next, as shown in FIG. 1B, 100 nm of a Ti film was deposited as a metallic film 3 on the AlN crystal film which is a group III nitride crystal film 2 by an evaporation method. Subsequently, as shown in FIG. 1C, the resultant article was thermally treated for 30 minutes at 1000° C. in an atmosphere of NH₃ gas in an oven (in Example 1, HVPE oven) for growing the crystal of the group III nitride crystal. By such thermal treatment as described above, a pore 4 h was formed in the metallic film 3 while a void portion 2 b was formed in the AlN crystal film which is the group III nitride crystal film 2. When the surface of the metallic film was analyzed by X-ray Diffraction (hereinafter, referred to also as “XRD”), it was found that the TiN film was formed.

Thereafter, as shown in FIGS. 1D and 1E, an AlN crystal which is each of a group III nitride crystal 5 for filling and a group III nitride crystal 6 was grown by using A₁ and NH₃ as a group III raw material and a nitrogen raw material, respectively, by using a Hydride Vapor Phase Epitaxy (hereinafter, referred to also as “HVPE”) method. On this occasion, an HCl gas was used as a carrier gas for Al; 40% of an H₂ gas based on the NH₃ gas which is a nitrogen raw material gas was used as an oxygen reducing agent; and a plate made of carbon having a unit surface area of 200 cm²/m³ was used. Growth of the AlN crystal by the HVPE method first appeared preferentially in the void portion 2 b of the AlN crystal film passing through the pore 4 h in the metallic film, to thereby fill the void portion 2 b. Thereafter, 400 μm of an AlN crystal which is the group III nitride crystal 6 was grown on a Ti film on a surface of which the TiN film which is the metallic nitride film 4 was formed. The resultant AlN crystal showed a Full Width Half Maximum (hereinafter, referred to also as “FWHM”) value of 90 arsec by XRD and a dislocation density of 6×10⁷ cm⁻² by TEM observation. The results are collectively shown in Table I.

Examples 2 to 6

A group III nitride crystal was prepared in the same manner as in Example 1 under the conditions shown in Table I or II, and then, was subjected to measurements of an FWHM value by XRD and a dislocation density. The results are collectively shown in Table I or II. TABLE I Example 1 Example 2 Example 3 Substrate Sapphire Sapphire Sapphire Group III nitride crystal film Growth Growth method MOCVD MOCVD MOCVD condition Group III raw TM-Al TM-In TM-Ga (90) material (mol %) TM-In (10) Nitrogen raw NH₃ NH₃ NH₃ material Film Crystal composition AlN InN Ga_(0.9)In_(0.1)N Film thickness (nm) 200  50  50 Metallic film Deposition Deposition method Evaporation Evaporation Evaporation condition Raw material Ti Ti Ti-Al Generated Film composition Ti Ti Ti-Al film Film thickness (nm) 100  30 300 Thermal Processing gas NH₃ NH₃ NH₃ (80) treatment N₂ (20) Metallic film after Film composition TiN TiN Ti_(0.5)Al_(0.5)N subjected to Void ratio (%)  33  12  18 thermal treatment Group III nitride crystal Growth condition Growth method HVPE MOCVD MOCVD Group III raw material (mol %) Al TM-In TM-Ga (90) TM-In (10) Nitrogen raw material NH₃ NH₃ NH₃ Reducing H₂ as (mol %)  40  10  10 agent Unit surface area of 200 — 200 carbon (cm²/m³) Oxygen concentration (mol %)  0.003  0.03  0.06 Crystal Property Crystal composition AlN InN Ga_(0.9)In_(0.1)N Thickness (μm) 400  5  10 FWHM (arsec)  90 180 160 Dislocation density (cm⁻²) 6 × 10⁷ 8 × 10⁸ 3 × 10⁸

TABLE II Example 4 Example 5 Example 6 Substrate SiC GaAs Sapphire Group III nitride crystal film Growth Growth method MOCVD MOCVD MOCVD condition Group III raw TM-Al (40) TM-Ga TM-Al (15) material (mol %) TM-Ga (60) TM-Ga (80) TM-In (5) Nitrogen raw NH₃ NH₃ NH₃ material Film Crystal composition Al_(0.4)Ga_(0.6)N GaN Al_(0.15)Ga_(0.8)In_(0.05)N Film thickness (nm) 200 500 300 Metallic Film Deposition Deposition method Evaporation Evaporation Evaporation condition Raw material V V-Fe Ti Generated Film composition V V Ti film Film thickness (nm) 800 300 500 Thermal Processing gas N₂ NH₃ NH₃ treatment Metallic film after Film composition VN VN TiN subjected to Void ratio (%) 36 21 34 thermal treatment Group III nitride crystal Growth condition Growth method HVPE HVPE MOCVD Group III raw material (mol %) Al (40) Ga TM-Al (15) Ga (60) TM-Ga (80) Tm-In (5) Nitrogen raw material NH₃ NH₃ NH₃ Reducing H₂ as (mol %) 30 50 40 agent Unit surface area of — 1000 — carbon (cm²/m³) Oxygen concentration (mol %) 0.02 0.006 0.01 Crystal Property Crystal composition Al_(0.4)Ga_(0.6)N GaN Al_(0.15)Ga_(0.8)In_(0.05)N Thickness (μm) 250 300 10 FWHM (arsec) 120 70 130 Dislocation density (cm⁻²) 5 × 10⁷ 6 × 10⁵ 9 × 10⁷

Comparative Example 1

Firstly, 10 nm of a buffer layer of AlN was grown at an ambient temperature of 500° C. and, subsequently, 100 μm of an AlN crystal was grown at an ambient temperature of 1000° C. on a sapphire substrate by using an HVPE method. On this occasion, A₁ and NH₃ were used as a group III raw material and a nitrogen raw material, respectively. Further, 50% of an H₂ gas based on a NH₃ gas which is a nitrogen raw material gas was used as an oxygen reducing agent and a plate made of carbon having a unit surface area of 1000 cm²/m³ was used. The resultant AlN crystal showed an FWHM value of 220 arsec by XRD and a dislocation density of 8×10⁹ cm⁻² by TEM observation.

Comparative Example 2

After an Al crystal film and a Ti film were formed on a sapphire substrate in the same manner as in Example 1, the resultant article was thermally treated. Thereafter, an AlN crystal was grown thereon by using an HVPE method. On this occasion, Al, an NH₃ gas and an HCl gas were used as a group III raw material, a nitrogen raw material and a carrier gas for Al, respectively. However, an oxygen reducing agent such as an H₂ gas or carbon was not used and the oxygen concentration was 0.5%. On this occasion, the AlN crystal was not obtained.

Example 7

500 μm of a Al_(0.4)Ga_(0.6)N crystal was further grown on the Al_(0.4)Ga_(0.6)N crystal obtained in Example 4 in an atmosphere of an oxygen concentration of 0.02% by mol by using 40% by mol of Al and 60% by mol of Ga as group III raw materials and an NH₃ gas as a nitrogen raw material by means of an HVPE method. On this occasion, an HCl gas was used as a carrier gas for each Al and Ga and 30% of an H₂ gas based on the NH₃ gas which is a nitrogen raw material gas was used. The Al_(0.4)Ga_(0.6)N crystal obtained in the present Example showed an FWHM value of 82 arsec by XRD and a dislocation value of 8×10⁶ cm⁻² by TEM observation.

As shown in Examples 1 to 6 in Tables I and II, the group III nitride crystal film and the metallic film were formed on the substrate, and then, after the resultant article was thermally treated, by forming an atmosphere of an oxygen concentration of 0.1% by mol or less when a group III nitride crystal for filling and a group III nitride crystal were grown, the group III nitride crystal having a dislocation density of less than 1×10⁹ cm⁻² and good quality was obtained. Further, by forming an atmosphere of an oxygen concentration of 0.01% by mol or less, a group III nitride crystal having a dislocation density of 1×10⁸ cm² and good quality was obtained.

In contrast, since Comparative Example 1 forms the group III nitride crystal film and the metallic film but does not comprise the step of the thermal treatment, the dislocation density became as large as 8×10⁹ cm⁻², and, in Comparative Example 2, since the oxygen concentration at the time of forming the group III nitride crystal for filling and a group III nitride crystal became over 0.1% by mol, the AlN crystal which is a group III nitride crystal was not obtained.

Further, as shown in Example 7, by growing a group III nitride crystal on the group III nitride crystal by the production method according to the present invention, the group III nitride crystal having a dislocation density of less than 1×10⁸ cm⁻² and good quality was obtained.

It is to be understood that embodiments and examples disclosed herein are illustrative and not restrictive in all aspects. The scope of the invention should be determined with reference to the appended claims and not to the above descriptions and is intended to include meanings equivalent to such claims and all such modifications and variations as fall within the scope of such claims.

INDUSTRIAL APPLICABILITY

As has been described above, according to the present invention, by forming a group III nitride crystal film and a metallic film on a substrate, and then, after the resultant article is thermally treated, forming an atmosphere of an oxygen concentration of 0.1% by mol or less when a group III nitride crystal for filling and a group III nitride crystal were grown, not only a GaN crystal, but also a group III nitride crystal having a small dislocation density and good quality and a production method therefor can be provided. 

1. A production method for a group III nitride crystal, being characterized by comprising the steps of: growing a group III nitride crystal film on a substrate; depositing a metallic film on the group III nitride crystal film; not only generating a pore in the metallic film but also forming a void portion in the group III nitride crystal film by thermally treating the substrate on which the group III nitride crystal film is grown and the metallic film is deposited; growing a group III nitride crystal for filling on the group III nitride crystal film in which the void portion is formed in an atmosphere of an oxygen concentration of 0.1% by mol or less to fill the void portion in the group III nitride crystal film; and growing a group III nitride crystal on the metallic film in an atmosphere of an oxygen concentration of 0.1% by mol or less.
 2. A production method for a group III nitride crystal, being characterized by comprising the steps of growing a group III nitride crystal film on a substrate; depositing a metallic film on the group III nitride crystal film; not only changing the metallic film into a metallic nitride film and, further, generating a pore in the metallic film, but also forming a void portion in the group III nitride crystal film by thermally treating the substrate on which the group III nitride crystal film is grown and the metallic film is deposited; growing a group III nitride crystal for filling on the group III nitride crystal film in which the void portion is formed in an atmosphere of an oxygen concentration of 0.1% by mol or less to fill the void portion in the group III nitride crystal film; and growing a group III nitride crystal on the metallic nitride film in an atmosphere of an oxygen concentration of 0.1% by mol or less.
 3. The production method for the group III nitride crystal as set forth in claim 1 or 2, being characterized by forming the atmosphere of an oxygen concentration of 0.1% by mol or less at the time of growing the group III nitride crystal for filling and/or the group III nitride crystal, by at least one of a method of using an H₂ gas and a method of using carbon.
 4. The production method for the group III nitride crystal as set forth in any one of claims 1 to 3, wherein the group III nitride crystal is an Al_(x)Ga_(y)In_(1-x-y)N crystal (0≦x, 0≦y, x+y≦1).
 5. The production method for the group III nitride crystal as set forth in any one of claims 1 to 4, wherein the metallic film comprises titanium, vanadium or an alloy comprising at least one of titanium and vanadium.
 6. The production method for the group III nitride crystal as set forth in any one of claims 1 to 5, wherein thickness of the metallic film is from 10 nm to 1000 nm.
 7. The production method for the group III nitride crystal as set forth in any one of claims 1 to 6, being characterized by further removing the substrate to obtain only the group III nitride crystal grown on the metallic film of the substrate.
 8. A production method for a group III nitride crystal, being characterized by further comprising the step of growing a group III nitride crystal in an oxygen atmosphere of 0.1% by mol or less on the group III nitride crystal obtained by the method as set forth in any one of claims 1 to
 7. 9. A group III nitride crystal, being obtained by the method for obtaining the group III nitride crystal as set forth in any one of claims 1 to
 8. 